Biodegradable thermoplastic material designed for injection molding applications
to order biogranucat please contact us by phone or e-mail
Product description Processing conditions Packaging Storage Form/Color NOPLA 102 Biodegradable thermoplastic material for injection molding applications PRODUCT TECHNICAL SHEET Date: 07.2023 Thermoplastic material of 100% biological origin, produced from annually renewable plant resources, GMO-free. Designed for injection molding applications. Under natural conditions, it is fully biodegradable and compostable. The material is designed for injection molding, including packaging in contact with food. The product has hygroscopic properties, so it is supplied in airtight packaging that should be unsealed immediately before use. It is not required to dry the product before processing. However, it is advisable to protect the granules from moisture at any stage of processing, as well as during storage in unsealed packages. Processing parameters: Feed zone temperature below 30°C Plasticizing zone temperature in the range of 160-200°C Mold temperature below 30°C The material is not compatible with plastics, so cleaning of the injection system is required to avoid microplastic contamination. Do not overheat the material above 200°C. It is advisable to prevent long-term stagnation of the material in the cylinder, otherwise thermal degradation may occur, which will lead to production instability and deterioration of product properties. The product is in the form of beige-colored granules. Only carry out staining based on the staining concentrates provided by the manufacturer. Store granules in airtight containers in a dry and cool place away from direct sunlight and any external heat sources. The package must be tightly closed until the material is used and resealed after use to avoid waterlogging. If the granules are soggy, it is recommended to dry them before use for at least 3 h, at 60°C. Barrier: 25 kg bag, 1000 kg big-bag, 1000 kg octobin
TYPICAL PROPERTIES UNIT NOMINAL VALUE* Physical Density MFR (190°C, 2.16 kg) MVR (190°C, 2,16 kg) g/cm3 g/10 min cm3/10 min PN-EN ISO 1183-1 PN-EN ISO 1133 TEST METHOD Mechanical Tensile strength Elongation at break Modulus of elasticity at tension Modulus of elasticity at bending Notched impact strength by Charpy Notched impact strength by Izod MPa % GPa MPa GPa kJ/m2 kJ/m2 PN-EN ISO 527 PN-EN ISO 178 PN-EN ISO 179-1 PN-EN ISO 180 Thermal Softening temperature by Vicat, method A/10 HDT – temperature of deflection under load, method B (0.45 MPa) °C 54 °C PN-EN ISO 306 PN-EN ISO 75-2
* Typical nominal values are given for informational purposes only and should not be considered as specifications. 5 1,29 41 36 34 4 1,3 48 2,4 8 7 61